N 29-9特殊钢堆焊焊条 日本日亚模具焊条蓝翔恒达15901248886经理
日亚不锈钢焊接材料
品名
| 熔敷金属化学成分之一例(Wt%)
| 拉伸强度
| 日亚商标
| C
| Si
| Mn
| P
| S
| Ni
| Ci
| Other
| N/mm㎡
| Kfg/m㎡
| E308L-16
| ≤0.033
| ≤0.33
| ≤1.34
| -
| -
| ≤9.90
| -
| Cr≤19.20
| ≥541
| ≥45
| NSR-308A
| E316L-16
| ≤0.035
| ≤0.54
| ≤1.62
| -
| -
| ≤13.21
| -
| Cr≤19.48
| ≥540
| ≥41
| NSR-316L
| E308
| ≤0.08
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 9.0～11.0
| 18.0～21.0
| -
| ≥550
| ≥56
| NS-308,NSN308,HS-308
| NSD-308,NSV-308,NSR308
| E308L
| ≤0.04
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 9.0～12.0
| 18.0～21.0
| -
| ≥510
| ≥52
| NS-308,NS-308L,NSR-308L
| NSD-308L,NS-309
| E309
| ≤0.15
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 9.0～14.0
| 22.0～25.0
| -
| ≥550
| ≥56
| NS-309,NSN-309,HRS-309
| NSD-309,NS-309
| E309L
| ≤0.04
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 12.0～16.0,
| 22.0～25.0
| -
| ≥510
| ≥56
| NS-309,NSN-309L
| E308cb
| ≤0.12
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 12.0～14.0
| 22.0～25.0
| Nb0.70～1.00
| ≥550
| ≥56
| NS-309cb
| E308Mo
| ≤0.12
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 12.0～14.0
| 25.0～28.0
| Mo2.00～3.00
| ≥550
| ≥56
| MS309-MO,NSN-309MO
| E310
| ≤0.20
| ≤0.09
| ≤2.50
| ≤0.030
| ≤0.030
| 20.0～22.0
| 25.0～32.0
| -
| ≥550
| ≥56
| NS-310,NSN-310,NSD310
| E312
| ≤0.15
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 8.0～10.5
| 28.0～32.0
| -
| ≥660
| ≥67
| NS-312,NSN-312
| E316
| ≤0.08
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 11.0～14.0
| 17.0～20.0
| Mo2.00～2.75
| ≥550
| ≥56
| NS-316,NSN-316-HSR-316
| NSD-316,HS-316
| E316L
| ≤0.04
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 11.0～16.0
| 17.0～20.0
| Mo2.00～2.75
| ≥510
| ≥52
| NS-316L,NSN-316,HSR-316L
| NSD-316L,HS-316L
| E317
| ≤0.08
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 12.0～14.0
| 18.0～21.0
| Mo3.00～4.00
| ≥550
| ≥56
| NS-317
| E317L
| ≤0.04
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 12.0～16.0
| 18.0～21.0
| Mo3.00～4.00
| ≥510
| ≥52
| NS-317L
| E347
| ≤0.08
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| 9.0～11.0
| 18.0～21.0
| Nb8×C%～1.00
| ≥550
| ≥56
| MS-347,NSN-347
| E310
| ≤0.12
| ≤0.09
| ≤2.50
| ≤0.040
| ≤0.030
| ≤0.60
| 11.0～14.0
| -
| ≥480
| ≥49
| NS-4
|
|
| 备注 : |
因不锈钢传热慢,使用一般不锈钢焊接后,
焊缝附近有很多飞溅,此些飞溅极难清除.
若使用日亚NSR焊条,此问题便可容易解决,
因为日亚牌不锈钢焊条飞溅极少
|
N 29-9特殊钢堆焊；接合使用
| 特性 | N29-9为添加特殊元素高氧化性钛型焊条，操作性能极好，熔敷金属为以Fe,Ni,Cr为主要元素的双层组织，焊后具有硬度低，高强度、高韧性等特点。耐酸化氧化性能X良，同时又有耐热、耐腐蚀、耐冲击磨耗等特点；适用于特殊材料的修补、堆焊；或者堆焊的衬焊使用 |
| 用途 | 铸钢的焊接；耐腐蚀、耐热堆焊；耐冲击磨耗；工具钢；冲压模；高低压铸造模；塑胶模等高裂性的材料的焊接和衬焊 |
| 操作要X | 为防止裂纹，尽量使用低电流，过大电流会引起烧棒；高合金钢特种钢200℃以上预热；摆焊幅度在棒径2.5倍左右；使用前250℃烘干 |
| 技术参数 | 抗拉强度 804N/mm2 | 伸长20.5% | 硬度 260 Hv 22HrC |