PBT1100台湾长春企业集团 物性数据 |
规格X别: | 一般X | 外观颜色: | 本色 |
用途概述: | 合胶原料、扣件组具、电脑键盘、文具外壳、旋扭开关。 | ||
备注说明: | 产品特性:粘度较大、物性强韧、成型品表面光滑。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||||
物理性能 | 比重 | --- | ASTM D792 | 1.30-1.32 | --- | ||||||||||
吸水率 | 24hr immersion | ASTM D570 | 0.06 | % | |||||||||||
|
|
|
|
| |||||||||||
玻璃纤维含量 | --- | Ash | 0 | % | |||||||||||
机械性能 | 引张强度 | --- | ASTM D638 | 500-600 | kg/cm2 | ||||||||||
引张伸长率 | --- | ASTM D638 | 120-180 | % | |||||||||||
挠曲强度 | --- | ASTM D790 | 750-850 | kg/cm2 | |||||||||||
挠曲强度 | --- | ASTM D790 | 750-850 | kg/cm2 | |||||||||||
挠曲弹性率 | --- | ASTM D790 | ≥20000 | kg/cm2 | |||||||||||
IZOD冲击强度 | 切口1/4″ | ASTM D256 | 5.0-6.0 | kg-cm/cm | |||||||||||
硬度 | --- | ASTM D785 | 85-90 | M-Scale | |||||||||||
电气性能 | 诱电率 | --- | ASTM D150 | 3.3 | 60Hz | ||||||||||
诱电正接 | --- | ASTM D150 | 0.001 | 60Hz | |||||||||||
体积抵抗率 | --- | ASTM D257 | >1015 | Ω-cm | |||||||||||
表面抵抗率 | --- | ASTM D257 | >1013 | Ω | |||||||||||
绝缘破坏强度 | 2mm | ASTM D149 | >20 | KV/mm | |||||||||||
耐电弧性 | --- | ASTM D495 | 120 | sec | |||||||||||
热 性 能 | 耐燃性 | 0.75mm | UL94 | HB | --- | ||||||||||
热变形温度 | 18.6kg/cm2(4.6kg/cm2) | ASTM D648 | 60(155) | ℃ | |||||||||||
线膨胀系数 | --- | ASTM D696 | 9 | 10-5cm/cm℃ | |||||||||||
融点 | --- | DSC | 225 | ℃ |
PBT 基础创新塑料(美国) IQNH4550-BK1066
PBT 基础创新塑料(美国) SHF434HR-BK1066
PBT 基础创新塑料(美国) SHF4930-BK1066
PBT 基础创新塑料(美国) U3900WX-BK1066
PBT 基础创新塑料(美国) WFC4033-GR
PBT 基础创新塑料(美国) WX05502-GY LTNRT
PBT 基础创新塑料(美国) WX05502-GYLTWRT
PBT 基础创新塑料(美国) 420SEO-GY4D225
PBT 基础创新塑料(美国) 2735 BK1066
PBT 基础创新塑料(美国) 310-1001
热塑性塑料在溶剂中会发生溶胀,但一般不溶于冷溶剂,在热溶剂中,有些热塑性塑料会发生溶解,如聚乙烯溶于二甲苯中,热固性塑料在溶剂中不溶,一般也不发生溶胀或仅轻微溶胀,弹性体不溶于溶剂,但通常会发生溶胀。